SPERANZA, Vito ;VIETRI, Umberto ;PANTANI, Roberto . Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts. Strojniški vestnik - Journal of Mechanical Engineering, [S.l.], v. 59, n.11, p. 677-682, june 2018. ISSN 0039-2480. Available at: <https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/>. Date accessed: 19 nov. 2024. doi:http://dx.doi.org/10.5545/sv-jme.2013.1000.
Speranza, V., Vietri, U., & Pantani, R. (2013). Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts. Strojniški vestnik - Journal of Mechanical Engineering, 59(11), 677-682. doi:http://dx.doi.org/10.5545/sv-jme.2013.1000
@article{sv-jmesv-jme.2013.1000,
author = {Vito Speranza and Umberto Vietri and Roberto Pantani},
title = {Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts},
journal = {Strojniški vestnik - Journal of Mechanical Engineering},
volume = {59},
number = {11},
year = {2013},
keywords = {injection molding; quality control; shrinkage},
abstract = {In this work, a series of injection moulding tests were conducted using a general purpose PolyStyrene, PS, and changing the holding pressure, injection temperature and cavity dimensions. The pressures at the interface with the mould at several positions along the flow-path were measured by means of pressure-temperature transducers. The samples were measured after moulding to determine dimensional accuracy, which was taken to be the target quality parameter. The pressure profiles obtained were then analysed using a recently developed procedure that is able to estimate the local solidification history from pressure measurements. The local average solidification pressure, namely the average along the thickness direction of the pressures at which each layer solidifies, could thus be estimated. This parameter is known to correlate well with shrinkage and thus a master-curve can be created that can be adopted to monitor the quality of the moulded part on line.},
issn = {0039-2480}, pages = {677-682}, doi = {10.5545/sv-jme.2013.1000},
url = {https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/}
}
Speranza, V.,Vietri, U.,Pantani, R. 2013 June 59. Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts. Strojniški vestnik - Journal of Mechanical Engineering. [Online] 59:11
%A Speranza, Vito %A Vietri, Umberto %A Pantani, Roberto %D 2013 %T Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts %B 2013 %9 injection molding; quality control; shrinkage %! Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts %K injection molding; quality control; shrinkage %X In this work, a series of injection moulding tests were conducted using a general purpose PolyStyrene, PS, and changing the holding pressure, injection temperature and cavity dimensions. The pressures at the interface with the mould at several positions along the flow-path were measured by means of pressure-temperature transducers. The samples were measured after moulding to determine dimensional accuracy, which was taken to be the target quality parameter. The pressure profiles obtained were then analysed using a recently developed procedure that is able to estimate the local solidification history from pressure measurements. The local average solidification pressure, namely the average along the thickness direction of the pressures at which each layer solidifies, could thus be estimated. This parameter is known to correlate well with shrinkage and thus a master-curve can be created that can be adopted to monitor the quality of the moulded part on line. %U https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/ %0 Journal Article %R 10.5545/sv-jme.2013.1000 %& 677 %P 6 %J Strojniški vestnik - Journal of Mechanical Engineering %V 59 %N 11 %@ 0039-2480 %8 2018-06-28 %7 2018-06-28
Speranza, Vito, Umberto Vietri, & Roberto Pantani. "Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts." Strojniški vestnik - Journal of Mechanical Engineering [Online], 59.11 (2013): 677-682. Web. 19 Nov. 2024
TY - JOUR AU - Speranza, Vito AU - Vietri, Umberto AU - Pantani, Roberto PY - 2013 TI - Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts JF - Strojniški vestnik - Journal of Mechanical Engineering DO - 10.5545/sv-jme.2013.1000 KW - injection molding; quality control; shrinkage N2 - In this work, a series of injection moulding tests were conducted using a general purpose PolyStyrene, PS, and changing the holding pressure, injection temperature and cavity dimensions. The pressures at the interface with the mould at several positions along the flow-path were measured by means of pressure-temperature transducers. The samples were measured after moulding to determine dimensional accuracy, which was taken to be the target quality parameter. The pressure profiles obtained were then analysed using a recently developed procedure that is able to estimate the local solidification history from pressure measurements. The local average solidification pressure, namely the average along the thickness direction of the pressures at which each layer solidifies, could thus be estimated. This parameter is known to correlate well with shrinkage and thus a master-curve can be created that can be adopted to monitor the quality of the moulded part on line. UR - https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/
@article{{sv-jme}{sv-jme.2013.1000},
author = {Speranza, V., Vietri, U., Pantani, R.},
title = {Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts},
journal = {Strojniški vestnik - Journal of Mechanical Engineering},
volume = {59},
number = {11},
year = {2013},
doi = {10.5545/sv-jme.2013.1000},
url = {https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/}
}
TY - JOUR AU - Speranza, Vito AU - Vietri, Umberto AU - Pantani, Roberto PY - 2018/06/28 TI - Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts JF - Strojniški vestnik - Journal of Mechanical Engineering; Vol 59, No 11 (2013): Strojniški vestnik - Journal of Mechanical Engineering DO - 10.5545/sv-jme.2013.1000 KW - injection molding, quality control, shrinkage N2 - In this work, a series of injection moulding tests were conducted using a general purpose PolyStyrene, PS, and changing the holding pressure, injection temperature and cavity dimensions. The pressures at the interface with the mould at several positions along the flow-path were measured by means of pressure-temperature transducers. The samples were measured after moulding to determine dimensional accuracy, which was taken to be the target quality parameter. The pressure profiles obtained were then analysed using a recently developed procedure that is able to estimate the local solidification history from pressure measurements. The local average solidification pressure, namely the average along the thickness direction of the pressures at which each layer solidifies, could thus be estimated. This parameter is known to correlate well with shrinkage and thus a master-curve can be created that can be adopted to monitor the quality of the moulded part on line. UR - https://www.sv-jme.eu/sl/article/monitoring-of-injection-moulding-of-thermoplastics-adopting-pressure-transducers-to-estimate-the-solidification-history-and-the-shrinkage-of-moulded-parts/
Speranza, Vito, Vietri, Umberto, AND Pantani, Roberto. "Monitoring of Injection Moulding of Thermoplastics: Adopting Pressure Transducers to Estimate the Solidification History and the Shrinkage of Moulded Parts" Strojniški vestnik - Journal of Mechanical Engineering [Online], Volume 59 Number 11 (28 June 2018)
Strojniški vestnik - Journal of Mechanical Engineering 59(2013)11, 677-682
© The Authors, CC-BY 4.0 Int. Change in copyright policy from 2022, Jan 1st.
In this work, a series of injection moulding tests were conducted using a general purpose PolyStyrene, PS, and changing the holding pressure, injection temperature and cavity dimensions. The pressures at the interface with the mould at several positions along the flow-path were measured by means of pressure-temperature transducers. The samples were measured after moulding to determine dimensional accuracy, which was taken to be the target quality parameter. The pressure profiles obtained were then analysed using a recently developed procedure that is able to estimate the local solidification history from pressure measurements. The local average solidification pressure, namely the average along the thickness direction of the pressures at which each layer solidifies, could thus be estimated. This parameter is known to correlate well with shrinkage and thus a master-curve can be created that can be adopted to monitor the quality of the moulded part on line.